Use of fly Ash a Substitute For Part Cement In Wall Plaster: An Effective Study on The Quality Tests of Plastering
DOI:
https://doi.org/10.37253/leader.v3i6.11971Keywords:
Fly Ash, Plaster, Compressive Strength, Cement , Environmentally Friendly.Abstract
Cement production in the construction industry generates a significant amount of carbon dioxide (CO2) emissions, which negatively impact the environment. One of the efforts to reduce this impact is by utilizing coal combustion waste (fly ash) as a partial replacement for cement. This study aims to determine the effect of using fly ash on the compressive strength of wall plaster and to identify the optimum percentage of fly ash substitution that still meets plaster quality standards. The research method used was a laboratory experiment with a quantitative approach. The variations of fly ash used were 20%, 30%, and 40% of the cement weight. Test specimens were cube - shaped with dimensions of 5 x 5 x 5 cm, and compressive strength tests were conducted at 7 and 21 days. The fly ash used in this study was obtained from the Sawah Lunto stream power plant PLTU Sawah Lunto). The results showed that the addition of fly ash affected the mechanical properties of the plaster, particularly its compressive strength. The highest compressive strength value was obtained from the mixture containing 20% fly ash, reaching 18.24 Mpa at 28 days of age.
Downloads
References
Amir, A. A., Parung, H., & Djamaluddin, R. (2020). Effect of aggregate characteristics on the compressive strength of high strength concrete. FROPIL (Forum Profesional Teknik Sipil), 11(1)
ASTM C39/C39M – 18. Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens. ASTM International.
ASTM C618. (2019). Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. ASTM International.
ASTM international. "ASTM C 618-19 Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete." Annual Book of ASTM Standards 2019 (2019).
Badan Standardisasi Nasional. Air untuk Campuran Beton (SNI 03-2847-2002).
Jakarta: Badan Standardisasi Nasional, 2002.
Danasi, Marsianus, and Ade Lisantono. "Pengaruh penambahan fly ash pada beton mutu tinggi dengan silica fume dan filler pasir kwarsa." Prosiding Konferensi Nasional Teknik Sipil 9 (2015).
Darmawan, Muhammad. "TA PENAMBAHAN FLY ASH SEBAGAI BAHAN CAMPURAN BETON NORMAL." Jutateks 3.1 (2019): 75-84.
Hansen, C. "Pemanfaatan Bahan Limbah untuk Campuran Bahan Plesteran." JURNAL ILMU PENGETAHUAN DAN TEKNOLOGI (IPTEK) 1.1 (2015): 18-27.
Kumar, R., Kumar, S., & Mehrotra, S. P. (2015). Influence of fly ash on the strength and durability of cement mortar. Construction and Building Materials, 96, 486–493.
Maryoto, Agus. "Pengaruh penggunaan high volume fly ash pada kuat tekan mortar." Jurnal Teknik Sipil dan Perencanaan 10.2 (2008): 103-114.
Mehta, P. K., & Monteiro, P. (2006). Concrete: microstructure, properties, and materials. (No Title).
Mehta, P. K., & Monteiro, P. J. M. (2014). Concrete: Microstructure, Properties, and Materials
(4th ed.). McGraw-Hill Education.
Neville, Adam M. Properties of concrete. Pearson Education India, 1963.
ONAIZI, ALI MOHAMMED AHMED SAGHIR, and UNIVERSITI TEKNOLGI MALAYSIA. ENHANCEMENT OF MECHANICAL PROPERTIES OF HIGH− VOLUME FLY ASH CONCRETE USING GLASS NANO POWDER AND EFFECTIVE
MICROORGANISMS. Diss. Universiti Teknologi Malaysia, 2022.
Pourkhorshidi, A. R., et al. "Applicability of the standard specifications of ASTM C618 for evaluation of natural pozzolans." Cement and Concrete Composites 32.10 (2010): 794-800.
SNI 03-1974-1990. Metode Pengujian Kuat Tekan Beton dengan Benda Uji Silinder. Badan Standardisasi Nasional (BSN).
.png){kind=small}